Effect of heat treatments on microstructure and mechanical properties of low-cost Ti-6Al-4V alloy produced by thermo-mechanical powder consolidation route

Singh, Ajit Pal and Torrens, Rob and Gabbitas, Brian and Sivaswamy, Giribaskar (2023) Effect of heat treatments on microstructure and mechanical properties of low-cost Ti-6Al-4V alloy produced by thermo-mechanical powder consolidation route. Metals, 13 (1). 173. ISSN 2075-4701 (https://doi.org/10.3390/met13010173)

[thumbnail of Singh-etal-metals-2023-Effect-of-heat-treatments-on-microstructure-and-mechanical -properties-of-low-cost-Ti-6Al-4V-alloy]
Preview
Text. Filename: Singh_etal_metals_2023_Effect_of_heat_treatments_on_microstructure_and_mechanical_properties_of_low_cost_Ti_6Al_4V_alloy.pdf
Final Published Version
License: Creative Commons Attribution 4.0 logo

Download (1MB)| Preview

Abstract

This paper investigates the level of properties enhancement achievable by heat-treating Ti-6Al-4V alloy produced from a blended powder mixture using a thermomechanical powder consolidation route involving warm uniaxial pressing and vacuum sintering followed by extrusion at super transus temperature (1150°C). The as-extruded material with a higher oxygen content of 0.55 wt.% was subjected to two different sub-transus annealing treatments: HT-A: 955°C/1h furnace cooling and HT-B: 925°C/4h-cooling @ 50°C/h to 760°C-FCfurnace cooling. Room temperature Charpy v-notch impact toughness tests and tensile tests were performed to ascertain the effect of microstructural changes during post-extrusion annealing treatments. After impact tests, analysis of microstructures and fracture surfaces of samples after impact tests were was carried out using optical microscopy and scanning electron microscopy. The as-extruded material displayed mean impact toughness of 4 J along with a yield strength of 956 MPa, an ultimate tensile strength of 22 1150 MPa, and an elongation to fracture of 2.4%. The annealing treatments gave a noticeable enhancement in the impact toughness (average values 5.3-6.3 J obtained) while maintaining a yield strength and ultimate tensile strength level of about 992 MPa and 1164-1181 MPa, respectively. Additionally, the level of change in ductility was limited for each sub-transus annealing treatment, and HT-A has given only a 30% increase compared to as-extruded material.