The influence of fibre length, diameter and concentration on the modulus of glass fibre reinforced Polyamide 6,6

Tools

Thomason, J.L. (2008) The influence of fibre length, diameter and concentration on the modulus of glass fibre reinforced Polyamide 6,6. Composites Part A: Applied Science and Manufacturing, 39 (11). pp. 1732-1738. ISSN 1359-835X (https://doi.org/10.1016/j.compositesa.2008.08.001)

[thumbnail of strathprints007310]
Preview
 Text. Filename: strathprints007310.pdf
Accepted Author Manuscript
Download (255kB)| Preview

Abstract

Results of an extensive investigation of the mechanical performance of injection moulded long glass fibre reinforced polyamide 6,6 composites are presented. The glass fibre content in these composites was varied over the range of 10-50% by weight using fibres with average diameters of 10, 14, and 17 μm. Mechanical testing was carried out at 23 and 150 °C on dry-as-moulded and boiling water conditioned samples. The results from these composites were compared with standard extrusion compounded short glass fibre materials. The influence of fibre diameter and concentration on the residual fibre length, fibre orientation distribution and composite modulus is presented and discussed in comparison to the predictions of some of the available micromechanical models.

ORCID iDs

Thomason, J.L. ORCID logoORCID: https://orcid.org/0000-0003-0868-3793;
CORE (COnnecting REpositories)