Analytical model of elastic fracture toughness for steel pipes with internal cracks

Tools

Yang, Shangtong and Li, Chun-Qing and Yang, Wei (2016) Analytical model of elastic fracture toughness for steel pipes with internal cracks. Engineering Fracture Mechanics, 153. pp. 50-60. ISSN 0013-7944 (https://doi.org/10.1016/j.engfracmech.2015.11.014)

[thumbnail of Yang-etal-EFM-2015-Analytical-model-of-elastic-fracture-toughness-for-steel-pipes]
Preview
 Text. Filename: Yang_etal_EFM_2015_Analytical_model_of_elastic_fracture_toughness_for_steel_pipes.pdf
Accepted Author Manuscript
License: Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 logo
Download (1MB)| Preview

Abstract

Corrosion or manufacture defects can cause internal cracks in steel pipes. For ductile materials, the crack front can yield before the stress intensity r eaches its fracture toughness. The yielding of the crack front could ease the stress concentration at the crack front. Therefore, to predict the failure of cracked steel pipes using linear elastic fracture m echanics it is necessary to quantify the part of fracture toughness that withstands the elastic stre ss field, namely, elastic fracture toughness. This paper intends to propose an analytical model of the elastic fracture toughness for steel pipes with internal surface cracks.