Xiong, C. and Rizzi, F. and Bejtka, K. and Edwards, P. R. and Gu, E. and Dawson, M. D. and Martin, R. W. and Watson, I. M. (2010) Fabrication and spectroscopy of GaN microcavities made by epitaxial lift-off. Superlattices and Microstructures, 47 (1). pp. 129-133. (https://doi.org/10.1016/j.spmi.2009.07.001)

Full text not available in this repository.Request a copy

Abstract

A novel epitaxial lift-off process for III-nitrides, involving selective removal of a sacrificial (Al, In)N layer in a hot nitric acid etchant, is reported. This was applied to the fabrication of 1−λ GaN planar microcavities bounded by two dielectric DBRs, starting from epitaxial GaN-(Al, In)N-GaN trilayers grown on free-standing GaN or high-quality GaN template material. An optically smooth surface was retained on the GaN surface exposed to the nitric acid etch, with root mean square roughness values as low as 2 nm over 8 μm×8 μm areas. Photoluminescence and reflectivity spectra were recorded from completed microcavities, and the latter showed clear dips in the region of 3.5 eV.