Microstructural, thermal, crystallization, and water absorption properties of films prepared from never-dried and freeze-dried cellulose nanocrystals

Tools

Hossain, Kazi M. Zakir and Calabrese, Vincenzo and da Silva, Marcelo A. and Schmitt, Julien and Bryant, Saffron J. and Islam, Md Towhidul and Felfel, Reda M. and Scott, Janet L. and Edler, Karen J. (2021) Microstructural, thermal, crystallization, and water absorption properties of films prepared from never-dried and freeze-dried cellulose nanocrystals. Macromolecular Materials and Engineering, 306 (1). 2000462. ISSN 1439-2054 (https://doi.org/10.1002/mame.202000462)

[thumbnail of Hossain-etal-MME-2021-Microstructural-thermal-crystallization-and-water-absorption-properties-of-films]
Preview
 Text. Filename: Hossain_etal_MME_2021_Microstructural_thermal_crystallization_and_water_absorption_properties_of_films.pdf
Final Published Version
License: Creative Commons Attribution 4.0 logo
Download (3MB)| Preview

Abstract

In this paper, the microstructural, optical, thermal, crystallization, and water absorption properties of films prepared from never-dried (ND) and freeze-dried (FD) cellulose nanocrystals (CNCs) are reported. Morphology of the ND CNCs reveals a needle-like structure, while after freeze-drying, they show a flake-like morphology. Microstructural analysis of ND and FD CNCs are further studied via small angle X-ray scattering to probe interactions. ND CNCs yield a transparent film with a low surface roughness (14 ± 4 nm), while the FD CNC film evidence a significant reduction of their transparency due to their higher surface roughness (134 ± 20 nm). Although Fourier transform infrared spectroscopy and energy-dispersive X-ray spectroscopy analyses reveal no chemical change occurs during the freeze-drying process, yet a more intense thermal degradation profile is observed for FD CNC film, probably due to the higher oxygen ingress within the gaps created between the stacked flakes. This, in turn, results in a greater loss of crystallinity at a higher temperature (300 °C) compared to the ND CNC film. A rapid decrease in water contact angle of the FD CNC film proves that the morphology of flakes and their orientation within the film has a strong influence in increasing water absorption capacity.