A nickel based superalloy reinforced by both Ni3Al and Ni3V ordered-fcc precipitates

Tools

Knowles, Alexander J and Reynolds, Lucy and Vorontsov, Vassili A and Dye, David (2019) A nickel based superalloy reinforced by both Ni3Al and Ni3V ordered-fcc precipitates. Scripta Materialia, 162. pp. 472-476. ISSN 1359-6462 (https://doi.org/10.1016/j.scriptamat.2018.12.013)

[thumbnail of Knowles-etal-SM-2018-A-nickel-based-superalloy-reinforced-by-both]
Preview
 Text. Filename: Knowles_etal_SM_2018_A_nickel_based_superalloy_reinforced_by_both.pdf
Accepted Author Manuscript
License: Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 logo
Download (17MB)| Preview

Abstract

A nickel based superalloy has been designed where the fcc γ Ni matrix is reinforced by two different ordered-fcc intermetallic compounds, γ' L12 Ni3Al and γ'' D022 Ni3V. Primary ageing at 900–1000 °C precipitated spherical L12 Ni3Al, whose volume fraction and size were controlled by altering the ageing temperature and time. Secondary ageing at 700 °C for 1–1000 h precipitated D022 Ni3V laths. The duplex precipitation increased hardness by up to 85 HV, with ∼ 500 MPa compressive proof strength maintained at 800 °C. Electron microscopy studied the Ni3Al precipitation and confirmed the form of the secondary Ni3V precipitates and their long term stability.