Accelerated ageing to study the degradation of cellulose nitrate museum artefacts

Quye, Anita and Littlejohn, David and Pethrick, Richard A. and Stewart, Robert (2011) Accelerated ageing to study the degradation of cellulose nitrate museum artefacts. Polymer Degradation and Stability, 96 (10). pp. 1934-1939. ISSN 0141-3910 (https://doi.org/10.1016/j.polymdegradstab.2011.06....)

Full text not available in this repository.Request a copy

Abstract

Cellulose nitrate is susceptible to hydrolysis as well as loss of plasticiser when left in a humid atmosphere. A comparison of the ageing behaviour of cellulose nitrate samples prepared from cotton linters was used to simulate the artefacts studied in a previous study. Certain artefacts were also subjected to accelerated ageing at 12%, 55% and 75% relative humidity at 70 degrees C. The rate of degradation was observed to vary with the RH, indicating the connection between the absorption of moisture and the hydrolysis process. The effect of varying the sulphate level on the rate of hydrolysis was studied using concentrations similar to those detected in artefacts. The study was carried out using <0.1 mg g(-1), 2 mg g(-1) and 5 mg g(-1) of sulphate and distinct differences were observed which is consistent with the conclusions drawn for a study of a number of artefacts. The observed rates of degradation are consistent with previous studies on cellulose nitrate. The degradation was studied using a combination of infrared spectroscopy, ion chromatography and gel permeation chromatography. The analysis was complemented by a study of the weight changes which occur during ageing. (C) 2011 Elsevier Ltd. All rights reserved.

ORCID iDs

Quye, Anita, Littlejohn, David ORCID logoORCID: https://orcid.org/0000-0002-1555-9427, Pethrick, Richard A. and Stewart, Robert;
CORE (COnnecting REpositories)