The effect of printing parameters on sintered properties of extrusion-based additively manufactured stainless steel 316L parts

Hassan, Waqar and Farid, Muhammad Asad and Tosi, Anna and Rane, Kedarnath and Strano, Matteo (2021) The effect of printing parameters on sintered properties of extrusion-based additively manufactured stainless steel 316L parts. International Journal of Advanced Manufacturing Technology, 114 (9-10). pp. 3057-3067. ISSN 1433-3015 (https://doi.org/10.1007/s00170-021-07047-w)

[thumbnail of Hassan-etal-IJAMT-2021-The-effect-of-printing-parameters-on-sintered-properties-of-extrusion-based-additively-manufactured]
Preview
 Text. Filename: Hassan_etal_IJAMT_2021_The_effect_of_printing_parameters_on_sintered_properties_of_extrusion_based_additively_manufactured.pdf
Accepted Author Manuscript
License: Strathprints license 1.0
Download (1MB)| Preview

Abstract

Extrusion-based additive manufacturing (EAM) is a relatively new process developed for the production of complex metallic and ceramic parts needed in smaller quantities. The debinding and sintering step of EAM is adopted from a well-known powder injection molding process. However, the 3D printing step needs special consideration to make EAM competent in the era of rapid manufacturing. This study is intended to investigate the effect of common printing parameters on the microstructure and mechanical properties of sintered stainless steel 316L (SS316L) parts manufactured through the EAM process. Part orientation (Ori), extrusion velocity (Ve), and layer height (h) were changed in experimental runs by following a full factorial design. Extrusion pressure as an indicator of melt stability and a grey relational grade as a combined response of sintered properties were analyzed against varying printing parameters. Physical characteristics measured during debinding and sintering show near isotopic shrinkage and the process is stable. Metallographic characterization in terms of porosity and grain size indicated minor differences when Ve and h were altered. Sintered parts showed improved properties when printed with vertical part orientation and h = 0.5 mm, whereas Ve which contributes significantly to the build-up rate was found to be responsible for melt stability. Ve at 12.5 mm/s exhibited melt stability and higher sintered properties.

ORCID iDs

Hassan, Waqar, Farid, Muhammad Asad, Tosi, Anna, Rane, Kedarnath ORCID logoORCID: https://orcid.org/0000-0002-9405-7950 and Strano, Matteo;
  • Item type:Article
    ID code:82338
    Dates:
    Date
    Event
    30 June 2021
    Published
    20 April 2021
    Published Online
    5 April 2021
    Accepted
    Subjects:UNSPECIFIED
    Department:UNSPECIFIED
    Depositing user: Pure Administrator
    Date deposited:13 Sep 2022 15:30
    Last modified:28 Nov 2024 01:25
    Related URLs:
    URI:https://strathprints.strath.ac.uk/id/eprint/82338
CORE (COnnecting REpositories)