Ultrafine grained plates of Al-Mg-Si alloy obtained by Incremental Equal Channel Angular Pressing : microstructure and mechanical properties

Lipinska, Marta and Chrominski, Witold and Olejnik, Lech and Golinski, Jacek and Rosochowski, Andrzej and Lewandowska, Malgorzata (2017) Ultrafine grained plates of Al-Mg-Si alloy obtained by Incremental Equal Channel Angular Pressing : microstructure and mechanical properties. Metallurgical and Materials Transactions A, 48 (10). 4871–4882. ISSN 1073-5623 (https://doi.org/10.1007/s11661-017-4258-8)

[thumbnail of Lipinska-etal-MMTA2017-Ultrafine-grained-plates-of Al-Mg-Si-alloy-obtained-by]
Preview
 Text. Filename: Lipinska_etal_MMTA2017_Ultrafine_grained_plates_of_Al_Mg_Si_alloy_obtained_by.pdf
Final Published Version
License: Creative Commons Attribution 4.0 logo
Download (2MB)| Preview

Abstract

In this study, an Al-Mg-Si alloy was processed using via Incremental Equal Channel Angular Pressing (I-ECAP) in order to obtain homogenous, ultrafine grained plates with low anisotropy of the mechanical properties. This was the first attempt to process an Al-Mg-Si alloy using this technique. Samples in the form of 3 mm-thick square plates were subjected to I-ECAP with the 90˚ rotation around the axis normal to the surface of the plate between passes. Samples were investigated first in their initial state, then after a single pass of I-ECAP and finally after four such passes. Analyses of the microstructure and mechanical properties demonstrated that the I-ECAP method can be successfully applied in Al-Mg-Si alloys. The average grain size decreased from 15 - 19 µm in the initial state to below 1 µm after four I-ECAP passes. The fraction of high angle grain boundaries in the sample subjected to four I-ECAP passes lay within 53-57 % depending on the examined plane. The mechanism of grain refinement in Al-Mg-Si alloy was found to be distinctly different from that in pure aluminium with the grain rotation being more prominent than the grain subdivision, which was attributed to lower stacking fault energy and the reduced mobility of dislocations in the alloy. The ultimate tensile strength increased more than twice, whereas the yield strength - more than threefold. Additionally, the plates processed by I-ECAP exhibited low anisotropy of mechanical properties (in plane and across the thickness) in comparison to other SPD processing methods, which makes them attractive for further processing and applications.