Tribological and corrosion performance of electrodeposited Ni–Fe/Al2O3 coating

Rezayat, Mohammad and Yazdi, Morteza Saghafi and Zandi, Mohammad Damous and Azami, Aref (2022) Tribological and corrosion performance of electrodeposited Ni–Fe/Al2O3 coating. Results in Surfaces and Interfaces, 9. 100083. (https://doi.org/10.1016/j.rsurfi.2022.100083)

[thumbnail of Rezayat-etal-RSI-2022-Tribological-and-corrosion-performance-of-electrodeposited]
Preview
 Text. Filename: Rezayat_etal_RSI_2022_Tribological_and_corrosion_performance_of_electrodeposited.pdf
Final Published Version
License: Creative Commons Attribution 4.0 logo
Download (3MB)| Preview

Abstract

Nickel–Iron coating was formed from a sulfate base electroplating bath under a current density of 3 A/dm 2 and turbulence of 300 rpm on a previously prepared cylindrical steel substrate. In order to obtain a sample including nickel composite coating, different amounts of alumina particle powder were added to the plating solution of the sample in question. By adding different quantities of ferrous sulfate to the electroplating bath under a current density of 2.5 A/dm 2 and turbulence of 300 rpm, an optimal sample containing 20 g/L of ferrous sulfate was obtained was free of any stress and microcracks. A hardness test was performed for the optimal sample among the nickel–iron​ composite samples, and the sample containing 50 g/L of alumina particles was selected as the optimal sample. The Ni–Fe/Al 2O3 composite sample was tested for hardness, corrosion and wear. The obtained results showed that the highest hardness level is equivalent to 740 HV and the best corrosion resistance with the most positive corrosion potential. The lowest amount of wear mass is equal to 0.1 mg, and it showed the highest wear resistance.