Enhanced surface energetics of CNT-grafted carbon fibers for superior electrical and mechanical properties in CFRPs

Badakhsh, Arash and An, Kay-Hyeok and Kim, Byung-Joo (2020) Enhanced surface energetics of CNT-grafted carbon fibers for superior electrical and mechanical properties in CFRPs. Polymers, 12 (6). 1432. ISSN 2073-4360 (https://doi.org/10.3390/polym12061432)

[thumbnail of Badakhsh-etal-Polymers-2020-Enhanced-surface-energetics-of-CNT-grafted]
Preview
 Text. Filename: Badakhsh_etal_Polymers_2020_Enhanced_surface_energetics_of_CNT_grafted.pdf
Final Published Version
License: Creative Commons Attribution 4.0 logo
Download (5MB)| Preview

Abstract

Surface enhancement of components is vital for achieving superior properties in a composite system. In this study, carbon nanotubes (CNTs) were grown on carbon fiber (CF) substrates to improve the surface area and, in turn, increase the adhesion between epoxy-resin and CFs. Nickel (Ni) was used as the catalyst in CNT growth, and was coated on CF sheets via the electroplating method. Surface energetics of CNT-grown CFs and their work of adhesion with epoxy resin were measured. SEM and TEM were used to analyze the morphology of the samples. After the optimization of surface energetics by catalyst weight ratio (15 wt.% Ni), CF-reinforced plastic (CFRP) samples were prepared using the hand lay-up method. To validate the effect of chemical vapor deposition (CVD)-grown CNTs on CFRP properties, samples were also prepared where CNT powder was added to epoxy prior to reinforcement with Ni-coated CFs. CFRP specimens were tested to determine their electrical resistivity, flexural strength, and ductility index. The electrical resistivity of CNT-grown CFRP was found to be about 9 and 2.3 times lower than those of as-received CFRP and CNT-added Ni-CFRP, respectively. Flexural strength of CNT-grown Ni-CFRP was enhanced by 52.9% of that of as-received CFRP. Interestingly, the ductility index in CNT-grown Ni-CFRP was 40% lower than that of CNT-added Ni-CFRP. This was attributed to the tip-growth formation of CNTs and the breakage of Ni coating.