EPRC is a leading institute in Europe for comparative research on public policy, with a particular focus on regional development policies. Spanning 30 European countries, EPRC research programmes have a strong emphasis on applied research and knowledge exchange, including the provision of policy advice to EU institutions and national and sub-national government authorities throughout Europe.

Explore research outputs by the European Policies Research Centre...

Selective adsorption of mixed organo silenes with differing reactive groups on E-glass surfaces

Liu, X.M. and Jones, F.R. and Thomason, James (2005) Selective adsorption of mixed organo silenes with differing reactive groups on E-glass surfaces. In: International Conference on Interfaces and Interphases in Multicomponent Materials 2005, 2005-09-12 - 2005-09-14, Centre Culturel Villeurbanne.

Full text not available in this repository. Request a copy from the Strathclyde author

Abstract

Organosilanes are often used in commercial sizings for glass fibres to provide wettability with the resin and promote strong interfacial adhesion to the matrix in a fibre reinforced polymer composite. The silane treatment is introduced as part of a complex deposition from an aqueous emulsion immediately at the spinaret and determines the optimum properties of the cured composite. To understand the interaction of organosilanes contained in sizings for glass surfaces, XPS was used to investigate the adsorption of γ-aminopropyltriethoxysilane (APS) from a simple sizing system containing a polyurethane (PU) film former. It has been found that both APS and the sizing (containing APS and PU) deposits on E-glass fibre surfaces contained components of differing hydrolytic stability. The differences observed in the AFM images of APS coated E-glass fibres before and after water extraction also confirmed that the APS deposit contained components with different water solubility.