Picture of UK Houses of Parliament

Leading national thinking on politics, government & public policy through Open Access research

Strathprints makes available scholarly Open Access content by researchers in the School of Government & Public Policy, based within the Faculty of Humanities & Social Sciences.

Research here is 1st in Scotland for research intensity and spans a wide range of domains. The Department of Politics demonstrates expertise in understanding parties, elections and public opinion, with additional emphases on political economy, institutions and international relations. This international angle is reflected in the European Policies Research Centre (EPRC) which conducts comparative research on public policy. Meanwhile, the Centre for Energy Policy provides independent expertise on energy, working across multidisciplinary groups to shape policy for a low carbon economy.

Explore the Open Access research of the School of Government & Public Policy. Or explore all of Strathclyde's Open Access research...

Analysing the effect of strain rate and temperature on the flow stress in AA1050 sheet using E-2448 standard

Allazadeh, Mohammad (2018) Analysing the effect of strain rate and temperature on the flow stress in AA1050 sheet using E-2448 standard. Journal of Multidisciplinary Engineering Science and Technology, 5 (11). pp. 9009-9015. ISSN 2458-9403

[img]
Preview
Text (Allazadeh-JMEST-2018-Analysing-the-effect-of-strain-rate-and-temperature)
Allazadeh_JMEST_2018_Analysing_the_effect_of_strain_rate_and_temperature.pdf
Final Published Version
License: Creative Commons Attribution 4.0 logo

Download (758kB)| Preview

    Abstract

    Uniaxial tests were performed to investigate the stress-strain relationship of aluminum alloy 1050 (AA1050) at different strain rates and forming temperatures. To this purpose, several coupons were cut from AA1050-H14 sheet with 2 mm thickness according to E-2448 standard in 0, 45, and 90 degrees with respect to the sheet`s rolling direction. The uniaxial tests were carried out in air and in argon gas at 100 oC, 200 oC, 300 oC, 400 oC, and 500 oC. The strain rates of the uniaxial tests were set for 0.001, 0.005, 0.0001, and 0.0005 s-1. The results show that altering the strain rate affects more the strength than the ductility attribute of AA1050 sheet. Moreover, the results reveal that ductility of AA1050 alloy has direct relationship with loading temperature, while AA1050 alloy’s strength has inverse relationship with the uniaxial testing temperature. The results were also investigated for the flow stress variation due to the loading direction and testing atmosphere. Laboratory test results suggested optimum parameters for forming part from AA1050-H14 alloy sheets of about 2 mm thickness at elevated temperature.