EBSD анализ микроструктуры аустенитной стали после прокатки в криогенных условиях

Aletdinov, Ainur and Mironov, Sergey and Korznikova, Galia and Zaripova, Rida and Konkova, Tatyana and Myshlyaev, Michail (2017) EBSD анализ микроструктуры аустенитной стали после прокатки в криогенных условиях. Materials Physics and Mechanics, 33 (1). pp. 29-40. ISSN 1605-2730 (https://doi.org/10.18720/MPM.3312017_4)

[thumbnail of Aletdinov-etal-MPM-2017-EBSD-analysis-of-austenite-steel-microstructure-after-cryogenic-rolling]
Preview
 Text. Filename: Aletdinov_etal_MPM_2017_EBSD_analysis_of_austenite_steel_microstructure_after_cryogenic_rolling.pdf
Accepted Author Manuscript
Download (1MB)| Preview

Abstract

This work is based on the use of electron backscatter diffraction (EBSD) methods to investigate the microstructure of metastable austeniticsteel 12X18H10T (321) after cryogenic rolling. Cryogenic deformation was accompanied by martensitic transformations, and the martensitic phase nucleation mainly in deformation bands. It is assumed that the proceeding of the martensitic transformation in the most deformed parts of the microstructure should prevent the evolution of deformation-induced boundaries in the austenite and, thus, inhibit the process of fragmentation of this phase. Mechanical twinning was the primary (or even sole) mechanism providing HAB formation in the austenite.

ORCID iDs

Aletdinov, Ainur, Mironov, Sergey, Korznikova, Galia, Zaripova, Rida, Konkova, Tatyana ORCID logoORCID: https://orcid.org/0000-0001-7495-7495 and Myshlyaev, Michail;
CORE (COnnecting REpositories)