Konkova, T. and Mironov, S. and Korznikov, A. and Korznikova, G. and Myshlyaev, M.M. and Semiatin, S.L. (2015) Annealing behavior of cryogenically-rolled Cu-30Zn brass. Journal of Alloys and Compounds, 648. pp. 858-863. ISSN 0925-8388 (https://doi.org/10.1016/j.jallcom.2015.05.287)

[thumbnail of Konkova-etal-JAC2015-Annealing-behavior-of-cryogenically-rolled-Cu-30Zn-brass]
Preview
 Text. Filename: Konkova_etal_JAC2015_Annealing_behavior_of_cryogenically_rolled_Cu_30Zn_brass.pdf
Accepted Author Manuscript
License: Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 logo
Download (1MB)| Preview

Abstract

The static-annealing behavior of cryogenically-rolled Cu-30Zn brass over a wide range of temperature (100-900 °C) was established. Between 300 and 400 °C, microstructure and texture evolution were dominated by discontinuous recrystallization. At temperatures of 500 °C and higher, annealing was interpreted in terms of normal grain growth. The recrystallized microstructure developed at 400 °C was ultrafine with a mean grain size of 0.8 μm, fraction of high-angle boundaries of 90 pct., and a weak crystallographic texture.