Should residual stresses be taken into account in structural integrity assessment of offshore monopiles?
Jacob, Anais and De Oliveira, Jeferson Araujo and Mehmanparast, Ali and Hosseinzadeh, Foroogh and Berto, Filippo; (2018) Should residual stresses be taken into account in structural integrity assessment of offshore monopiles? In: Structures, Safety, and Reliability. Proceedings of the International Conference on Offshore Mechanics and Arctic Engineering - OMAE . American Society of Mechanical Engineers (ASME), ESP. ISBN 9780791851227 (https://doi.org/10.1115/OMAE2018-78519)
Preview |
Text.
Filename: Jacob_etal_SSR_2018_Should_residual_stresses_be_taken_into_account_in_structural_integrity_assessment.pdf
Accepted Author Manuscript Download (629kB)| Preview |
Abstract
A key challenge in the Offshore Wind industry is assuring the life-cycle structural integrity of wind turbine foundation monopiles. This is due to harsh environmental aspects as well as the loading regime (i.e. constant exposure to wave and wind forces introducing both fatigue and corrosion damage). Welding is a widely used joining technique for the manufacturing of offshore monopile structures. However, this is an aggressive process that introduces high levels of residual stress, which in turn may lead to reduced fatigue life, corrosion cracking resistance and accelerated degradation mechanisms. This study presents evidence that a measurement-informed strategy could be used towards developing a more reliable structural integrity assessment procedure for offshore monopile structures by taking into account the effect of residual stresses. A welded mock-up, 90 mm thick, 2600 mm wide and 800 mm long plate, was fabricated using a typical double-V welding procedure following current industrial practice. The contour method of residual stress measurement was employed to map residual stresses in the welded mock-up as well as in the CT specimens extracted from the weld region of the plate for future fatigue tests. Residual stress measurement results show that the mock-up plate contained tensile residual stresses above yield in the core of the weld, while the extracted CT specimens had lower though still significant residual stress levels. These results indicate that if the initial residual stresses are not carefully considered during fatigue or corrosion cracking tests, the results from the CT specimens alone will likely result in misleading structural life estimations.
-
-
Item type: Book Section ID code: 79360 Dates: DateEvent25 September 2018Published26 March 2018AcceptedSubjects: Technology > Hydraulic engineering. Ocean engineering Department: Faculty of Engineering > Naval Architecture, Ocean & Marine Engineering Depositing user: Pure Administrator Date deposited: 28 Jan 2022 10:14 Last modified: 28 May 2024 00:35 Related URLs: URI: https://strathprints.strath.ac.uk/id/eprint/79360